LLS-09 anti-ant products developed by our company are mainly composed of a variety of pyrethrins and carbamate. Its appearance is white powder, melting point: 86-90℃, decomposition temperature ≥200℃, stable to light and heat. The product has been tested by EU ROHS directive and SVHC for high concern chemicals. It is a kind of low toxicity, high efficiency, long half-life of anti-ant agent, has a strong touch effect, strong knockdown force, rapid efficacy, prevention and control termites is particularly effective. Widely used in PVC and low smoke halogen-free plastic coating. Recommended dosage: 0.6-1.0%
Notes:
1.As LLS-09 anti - ant products have certain toxicity, do a good job of protection when using.
2.In contact with skin, rinse thoroughly with soap and water.
Storage:
The product is sealed and stored in a cool, dry and ventilated place.
The mechanical properties of termite resistant PVC coating plastic were tested as follows:
|
Testing item
|
Standard required
|
Testing result
|
Single conclusion
|
|
1.Mechanical properties tensile strength before aging (N/mm2)
|
≥12.5
|
19.7
|
qualified
|
|
Elongation at break (%)
|
≥150
|
300
|
qualified
|
|
2.Air tank after aging
|
|
|
|
|
Temperature (℃) 100±2, times (h)168
|
|
|
|
|
Tensile strength (N/mm2)
|
≥12.5
|
21.7
|
qualified
|
|
Rate of change (%)
|
≤±25
|
+9.7
|
qualified
|
|
Elongation at break (%)
|
≥150
|
350
|
qualified
|
|
Rate of change (%)
|
≤±25
|
16.6
|
qualified
|
|
3.Thermo-gravimetric experiment
|
|
|
|
|
Temperature (℃)80±2, times (h)168
|
|
|
|
|
Weightlessness (%)
|
≤2.0
|
0.34
|
qualified
|
|
4.Cracking test
|
|
|
|
|
Temperature (℃)-, times (h)-
|
|
|
|
|
Testing result
|
no cracking
|
no cracking
|
qualified
|
|
5.High temperature pressure test
|
|
|
|
|
Temperature (℃)80±2, times (h)4
|
|
|
|
|
Deformation rate (%)
|
≤50
|
22
|
qualified
|
|
6.Low temperature impact test
|
|
|
|
|
Temperature (℃)-15±2
|
|
|
|
|
Testing result
|
no cracking
|
no cracking
|
qualified
|
Extrusion process is stable, fast exit speed, uniform plasticization, smooth surface, no visible air holes, no peculiar smell.
|